Enamelling Weekend Workshop

 

It's only a few weeks to go now until our residential enamelling weekend in November!! We still have a couple of spaces on this if anyone else wants to join us. It is going to be a fun time with workshop sessions through from Friday afternoon to Sunday afternoon.

 

 

If you've ever wanted to learn more tips and techniques for working with silver clay and how to use enamels to add lovely vibrant colours to your work then don't miss out!!!

 

This workshop will be packed with great info and ideas for creating your own textures to enamel onto, adding stones to fire in place, decorating the back of your pieces and even adding super extra little finishing details like these fun little snakes on the side of the piece below.

 

 

The cost of this workshop includes your hotel stay and food plus you get an amazing 25g of Art Clay Silver to create with! All that for only £399 means it really is an excellent value weekend.

 

We will all eat together through the weekend so it's a chance for everyone to make new friends as well as learning new techniques. There is also a kit fee of £16 and as part of your kit you will get a range enamel colours ready prepared by me to use on the workshop and you get to take them home with you afterwards so you will be all set to carry on your enamelling adventure at home :D

 

You'll find all the details in this brochure :D

 

 This is the program for the weekend. As you can see it will be action packed with never a dull moment! ;)

If you are in Europe you'll find Folkestone is ideally situated right by the Channel Tunnel and there are also regular trains from London that only take around an hour.

 

I'm really looking forward to seeing old friends and new there :) If you have any questions about it do email me!!

 

Have fun!

 

Joy x

 

 

 

 

 



Hidden Lanterns and Joyful Spinners!

I am very excited to be going back over the pond to the USA next month to stay with my good friend, the very wonderful Ann Davis. My flights are all booked and it is only five weeks away!! Ann is a truly amazing and very innovative artist. I always feel so inspired when I stay with her and come back with my head crammed full of new ideas. She has done so many things and is a real fount of all knowledge!!! I always learn new things from her.

 

While I'm there I will be teaching for 3 days at Ann's studio - La Ruche Davis, near Washington, DC.

 

First will be a two day Hidden Lantern workshop. These are complex little pendants with lots of exciting techniques to learn. Each side of the hollow pendant is gently curved.  On the one side we will be making textured areas to enamel into. We will also be adding lovely sparkly accent stones.

 

 

The reverse of each pendant has pierced out areas in the design. This is why they are Hidden Lanterns ;) 

 

On two of the pendants 24k gold has been added inside which shines out through the pierced areas and reflects the light when they are worn that way round. The third pendant is a variation with a removable base. This allows for something different to be placed inside to show through. Of course for me that has to be something colourful!! :D

 

 

This pendant also has small accent stones set down each side.

 

 



One of my favourite parts of these pendants is the tops!!! Each has a different design and loop to hang it with. These really add to the character of each one.

 

I'll also be teaching a one day Joyful Spinner Rings workshop.

 

These fun rings are a delight to wear. Hours of twiddling fun with the inner ring freely moving inside the outer channelled one. There'll be lots of stone setting too to give them sparkle.

 

I've been making lots of examples of them - I love making these!!!

 

This one even has tiny stones set on the sides for even more sparkle!!!

 

I can't wait to see what everyone makes on these workshops. One of the things I enjoy so much about teaching is seeing people take an idea and come up with variations that would never even cross my mind!!!

 

If you want to join us for all the fun do get in touch very soon!! Both workshops are nearly full but there is still a seat or two left at the moment :D I'm looking forward to meeting old friends again and making new ones!!

 

I know I'll come home having learnt so much too!

 

Meanwhile - have fun!!

 

Joy x

 

 

 

 

 

 

 

 

 

Testing Art Clay Silver 950 Part 2

Part 2 of my Art Clay Silver 950 testing. Don't worry, there won't be a part 3 ;)

 

This will make a lot more sense if you have read Part 1 first, and if you've done that you will also know it is probably a good idea to grab a cup of tea before you start reading this time! Yes, it could be another long post! ;)

 

At the end of the last post I showed you two enamelled pieces. One was made out of AC950 (on the right) and depletion gilded. The one on the left was a circular piece of AC999 attached to a backing of AC950 and the two were fired together. I've now patinated these using Liver of Sulphur to bring up the textures. The LOS worked just fine, exactly as I would expect it to. Here they are all done. I love to patinate most things as it gives the textures definition and seems to make the enamel colours more vibrant :)

 

 

As I mentioned in the last blog post there is a difference between the shrinkage of AC950 and AC999. I've been trying to get a photo showing the slight doming on the piece on the left. As I've failed I decided to try a short video clip. I hope you might be able to see the domed effect in the centre of the back in this.

 

Next I made two more rings to see if the shrinkage seemed fairly consistent and also to try a few different techniques.

 

The first one is...um...a bit strange really! Why? Well I was using up the last bits of clay :D I forgot to take any process photos on this one so you'll have to stay with me here on a description.

 

 

I wanted to see how well the clay moulded. I twisted 2 strands of 1mm wire together and pressed it into two part moulding compound to make a long thin mould that I could use for a ring band. The clay moulded really well and cleanly. Then I added the front decoration. It looks kind of weird because it was all the bits I had left from all the other things I made. I'd made some tiny balls with little bits of clay and also I had two pieces left over for stone settings. I was going to use them on the first ring but changed my mind. So I set the two small barrel shapes with 2mm lab sapphires. I rolled out a tiny piece of clay .25mm (1 card) thick and once dry I added the ten tiny balls using water to join them. Once that piece was dry I sanded the tops off the balls to make that little piece in the middle.

Everything was joined using water only. After firing as per schedule I polished the ring and added some gold. Whenever I do keum boo I always totally polish the piece first then do the keum boo. The gold foil took really easily and without any issues.

Did I mention this was a tiny ring??? Actually it is a UK size N so perfectly wearable, just very thin!! Shrinkage was consistent with the first ring I made at 7 UK sizes. (As a side note I was amused to realise yet again I had created something vaguely bird like!!! or maybe I just see birds everywhere :D )

The third ring I made was more the sort of thing I would make normally. I started out with a snake of clay and then rolled it flat to 1.5mm (6 cards). I joined it into a flat band and once dry I carved it using a graver. I went with a quick simple starburst design to see how it felt. It carved very smoothly and cleanly. Lovely to work with!

 

Next I made a topper. I rolled out clay and textured a circle on both sides to .75mm (3 cards) thick. This is thinner than I would ever use in AC999 on a ring. I domed the circle by forming it over a 13mm bead to dry. Once dry I filed the edges to give a nice serrated look that went with the radiating design I had used.

 

I also filed the edges of the ring band.

 

The stone setting was a little piece I had pre-made in AC999. It was set with a 3mm lab ruby cab. I was interested to see how well the two clays would go together (and I was running short of clay to make a setting in AC950!). I used water to wet both parts and then joined them. It made a very solid join.

 

The topper was attached to the ring band using AC999 syringe. As I had used water only to join the toppers on my other two rings I wanted to see how this worked.

 

I fired the ring to schedule but took it out the kiln hot and placed it on one side to cool. The AC950 polished up very nicely. For this ring I used Black Max to patinate.

 

I was very pleased with the result. Again shrinkage was 7 UK sizes. I made this at a UK size X and it shrank to a UK size Q. After firing there was a certain amount of distortion, but that was very easy to correct on a ring mandrel, and because the fired silver is much harder I found there was less chance of marking it. The domed part held it shape nicely.

 

Finally I made one more piece to enamel. My other pieces had been more tests really so I wanted to make something that would show the colours better. I opted for one of my small butterfly designs.

 

I actually think the AC950 refines up even better than AC999 with baby wipes. Here is the dried butterfly before and after refining. The refining took me about 5 minutes, so very quick and easy.

 

 

This piece was textured to 1mm thick. Even though AC950 is stronger than AC999, for enamelling I would not make pieces any thinner. Enamel will crack on very thin silver unless you counter enamel the back due the stresses of the glass enamel on the silver. I never counter enamel as I always decorate the backs of things. For this little piece I stamped out one of my Joy logos. The AC950 took an impression from the stamp very crisply. I attached a piece of fine silver wire to the back of the piece using AC999 syringe to join it all.

 

 

This piece was fired to schedule at the same time as the previous ring. After firing I depletion gilded the piece until it was very white. Then I re-polished it and enamelled it.

 

And here it is...a rainbow butterfly!!!

 

So what conclusions did I draw from all this testing...

 

First of all - I love this clay!

 

 

Will I use it all the time?

No.

I'll still use AC999 for a lot of things. Depletion gilding works really well on AC950, but it does take extra time. If a piece needs extra strength I'll go with AC950 and put that extra time in if it is a piece to be enamelled. For rings I will definitely go over to AC950. If I am making something where the difference in strength will not be a major issue I'll stick with AC999.

 

For teaching I will most likely mainly stick to AC999 because of the shorter firing schedule, but there will be some things that I'll go over to AC950 for.

 

I'm  delighted to have had a chance to test this clay out - thank you Metal Clay Ltd!! I'm looking forward to the release date at the start of September so I can do more playing. I have lots of ideas in mind that I would not make using AC999 :)

 

If you use silver clay I recommend you give this a whirl and see what you think!!

 

Have fun!

 

Joy x

 



 

 



 

 

 

 



Testing Art Clay Silver 950 Part 1

I was very excited when Aida announced a new Art Clay Silver product recently. Art Clay Silver 950. The Art Clay (AC) I have been using up until now is fine silver which hallmarks at 999. This new silver clay is what being termed as enriched sterling silver clay. Traditionally sterling silver is 925 - that means for every thousand parts 925 of them are fine (pure) silver and the other 75 are something else - often copper. The new AC950 is (as you've probably guessed by now!) 950 parts fine silver and 50 parts copper, so this is enriched sterling as it has a higher percentage of silver in it. This makes a silver alloy that is stronger than fine silver. The other real plus is that AC950 can be fired open shelf, no carbon involved!!!

 

I was delighted to be asked by Metal Clay Ltd to test out the new clay pre-release. The clay will be available from 1st September and you can pre-order on their website.

 

 Here is how I got on with it. So...my lovely packet arrived and testing began :D

 

 

The clay felt slightly solider than AC999 on taking it out of the packet at first, but as soon as I kneaded it, it felt about the same as AC999. Rolling out and texturing were all very similar, drying took about the same length of time. It reconstituted well. Working with the dry clay it carved well and drilled well. If anything, to me it felt slightly stronger when working with the dry clay. MOST IMPORTANTLY baby wipes work beautifully with it for refining etc. Phew - anyone who knows me would know that would of been a real problem for me if they hadn't worked!!

 

I rolled out a piece of clay plain to .25mm thick and dried it naturally and the clay was very flexible. I cut some thin strips from the dry clay with scissors and it was possible to bend them into small links very easily. I didn't fire these as I only wanted to see how flexible the clay was.

 

 

Next I tried the same thing with a shallow texture on each side of the clay. This wasn't as flexible and broke easily on bending. This would need more testing to find the out the possibilities of using the clay like this.

 

I made a few small heart shapes. With any new clay checking out how the firing works is very important. Even though we were given a schedule for it there are always variables, not least the kiln that you use.

 

I fired just a couple of the little hearts first, and I made one using AC999 to fire at the same time. The firing schedule is from cold to 500°C with a 30 minute hold, then straight up to 870°C with a 60 minute hold. The instructions also say to leave pieces in the kiln until below 200°C. On my first pieces I did this. Here they are fresh out the kiln. You can see the difference in colour, AC999 in the middle and AC950 top and bottom.

 

 

 They seemed to fire well. I checked if they were sintered (fully fired) by putting a drop of water on the surface of each one. It stayed there nicely. If it had soaked straight in that would be an indication that the piece was not properly sintered. I also drew around the pieces before firing. This allowed me to check they had shrunk, another good indication of proper sintering. Then I bent one piece using pliers. It bent well and was noticeably harder to bend than the fine silver piece. The shrinkage on these little hearts appeared to be marginally more for AC950 than AC999. AC999 shrinks around 8%-10%. The packaging for the AC950 said shrinkage of 10%-13% so that seemed about right.

 

After these initial tests I wondered why the instructions suggested leaving the pieces in the kiln until it was below 200°C. If I was going to enamel pieces they would go in and out of the kiln at 800°C, so after that I didn't leave them to cool in the kiln. It could be there is a very good reason why they should be cooled in the kiln, but I didn't notice any difference by not doing it.

 

I fired the first pieces on ceramic fibre board and there was some slight marking on the backs of some of the pieces where it had stuck. I know my little kiln does run slightly hot so I fired the rest of the pieces at between 850°C and 860°C. There was still the odd bit of sticking on the second batch so after that I also fired on ceramic fibre paper. I think vermiculate would probably work well, but I didn't have any to hand.

 

For the next pieces I made a some more hearts and small ring. I made the ring at a UK size T.

 

 

After firing it had shrunk 7 sizes. After deformity correction I put it onto a mandrel and easily tapped up to a UK size N which is a shrinkage of 6 sizes. The band is 2 1/2mm wide and 1mm thick with a hammered texture that was rolled on when I made it in the clay. The stone is a 4mm lab ruby fired in place. The topper of the ring was attached to the band just using water and is really strongly attached (I hit it a few times with the hammer to check ;) ) The ring weighs in at just 1.45 grams!!! I was very impressed with this. There was quite a bit of distortion to the ring when it came out the kiln, but with the larger shrinkage that is to be expected really. It is very easy to re-round a ring.

 

 

As I often have my kiln running at 800°C plus when I'm enamelling I'm also in the habit of sometimes putting small pieces in to fire when the kiln is already hot. I placed one heart onto a hot kiln shelf at 870°C and put it straight back into the kiln just to see what happened. It was an interesting result! It went in flat and came out very domed! It also had less shrinkage. Whilst the water drop test seemed to show it was fairly sintered I suspect not all the binders burnt away so the piece had uneven shrinkage causing the curving. It is not something I would repeat!! ;)

 

 

I also tried to torch fire one piece. I used the torch to heat slowly to allow the binders to burn away first, and then took it up to orange and held it for 8 minutes. The piece had similar shrinkage to the kiln fired ones and appeared to be sintered. It bent to 90 degrees. This lead me to believe it might be possible to torch fire, but it would probably want a bit longer firing (maybe 2 x 5 minutes), and more testing to see if it would work on larger pieces.  

 

So...on to the crucial question...DOES IT ENAMEL???

 

The short answer is yes, but it is not quite that easy! ;)

 

I use transparent enamels all the time in my work. Opaques are generally less fussy and I suspect they will work direct onto AC950 but I haven't tested that. My tests are all using transparents :D

 

I did a several little test pieces first. In this photo are the results of different experiments.

 

 

Top left and middle right are direct onto polished AC950. The colours have changed and top left is going brown at the edges. The enamels colours should look like top right and middle left, turquoise blue and mid green. You can see they have really darkened when applied directly onto AC950.

 

Top right, middle left and bottom I added fine silver foil to the surface using the keum boo method. I didn't cover the whole of each heart, only part of it and you can see the difference. Whilst this might work on a plain piece I use textures all the while and it was immediately apparent this was not a viable solution on a textured surfaces. Because of this I didn't experiment any further with this idea.

 

Then  we come to the middle heart. This one has the same green as the other two in the middle row and the same red as the bottom piece.

 

Normally in enamelling we enamel on fine silver. If we use sterling sheet we either depletion gild or put the piece into nitric acid. The nitric acid eats away the copper at the surface and removes any firestain to leave a fine silver surface. I DID NOT want to use nitric acid - nasty stuff!!! So onto depletion gilding. This is a process of repeatedly heating a piece and then pickling it until the piece is bright white. The process creates a layer of fine silver up on the top surface of the piece, and this is what we want for enamelling. The middle heart was depletion gilded.  

 

Eureka! It worked just fine :D

 

Next I made  another couple of little pieces and depletion gilded them. You can see the flat heart and the bar are noticeably whiter than a piece of untreated AC950.

 

 

 All the colours again stayed nice and bright.

 

 

So would I use AC950 for enamelling? In some circumstances yes. It is horses for courses. If I can use AC999 for a piece I probably still will, but to be able to enamel AC950 after depletion gilding is a wonderful option where more strength is needed :D

 

Another thing I wanted to try out was combining AC999 with AC950. For this piece I made a textured backing of AC950 .75mm thick. I then made a circular textured piece in AC999 which was also .75mm thick. I attached the two together just using water. In the process of refining it I accidently broke it (oh sorry, make that - I deliberately broke it to see how well it would mend ;) lol). I again just used water to wet the breaks and the pieces reattached very easily. You can see the difference in the colour of the clays.

 

 

After firing and polishing the different colours are still visible. This also shows very clearly that the two clays do have different shrinkage rates (although maybe it doesn't show so clearly in the photo!) Where the AC999 is attached the piece has domed a little. I expected it to do that and I like the result.

 

 

Finally I enamelled this piece.

 



Today I've been using the last of the clay to make a couple more rings and another piece to enamel.  

 

I'll blog about those tomorrow!!! :D

 

If you've made it this far through the post - well done!!! ;) Go and have a cup of tea - you've earned it!!

 

Have fun!

 

Joy x

You can see the rest of my testing results in Testing Art Clay Silver 950 Part 2